Mechanical Properties of Titanium after Severe Plastic Deformation Mechanické vlastnosti titanu po extrémní plastické deformaci Doc. Ing. Miroslav Greger, CSc., Vysoká škola báňská Technická univerzita Ostrava, Ing. Ladislav Kander, Ph.D, MATERIÁLOVÝ A METALURGICKÝ VÝZKUM s.r.o., Ostrava This paper describes manufacture of ultra-grained titanium, its microstructure and properties. Ultra grained titanium has higher specific strength than ordinary (coarse-grained) titanium. Ultra-grained titanium was produced by the ECAP process. The research was focused on physical base of strengthening and softening processes and developments occurring at the grain boundaries during the ECAP process. Strength of ultra grained titanium varies around 960 MPa, grain size around 300 nm. V laborarních podmínkách byl připraven ultrajemnozrnný titan. Jemnozrnnost se získala aplikací technologie ECAP. Výchozím materiálem byla protlačovaná tyč z technicky čistého titanu (Ti Grade 1). Výchozí stav struktury byl po žíhání 649 C/1 h. Z tyče byly připraveny vzorky pro studium deformačního zpevnění a ECAP. Rozměry vzorků pro ECAP se vyznačovaly průměrem 30 mm, délkou 120 mm. Zařízení ECAP umožňovalo protlačovat vzorky z titanu a jeho slitin v intervalu teplot -10 C až 550 C. Na jednotlivých vzorcích se použil různý počet průchodů, od 1 až 9. Před jednotlivými průchody se vzorky pootáčelo kolem podélné osy, postupem Bc. Úhel kanálu byl 105. Po jednotlivých průchodech byly sledovány mechanické vlastnosti měřením tvrdostí HV 30, HV10, mikrotvrdosti HV0,1, tahovou zkouškou a pomocí penetračních testů. Cílem experimentů bylo zjistit intenzitu deformačního zpevnění po jednotlivých průchodech tj. v závislosti na kumulaci a teplotě deformace. Vývoj struktury a velikost zrna po deformacích byl sledován pomocí optické mikroskopie a pomoci RTG difrakce. Při průchodu vzorků matricí ECAP je struktura výrazně usměrněna pod úhlem 45 ke směru protlačování. Při kumulované deformaci kolem hodnoty 6 vzniká výrazná textura. Tvrdost titanu se zvyšuje v závislosti na teplotě protlačování. Při nízkých teplotách tvrdost intenzivně roste se zvyšujícím s počtem průchodů až do 4. průchodu kdy dosahuje hodnoty 180 HV10. V dalších průchodech je nárůst tvrdosti pozvolnější, po osmém průchodu se pohybuje kolem 200 HV10. Při studiu deformačního zpevnění, při rovinném stavu napjasti, v závislosti na velikosti deformace pomocí mikrotvrdosti HV0,1 je zpevnění lineární až do kumulované deformace 3,5. Při vyšších deformacích klesá. Příčinu poklesu tvrdostí nelze z provedených měření a analýz vysvětlit. Příčinou může být zotavení dislokační struktury při vyšší deformacích. Velikost zrna se s rosucí deformací zmenšuje. Z počáteční hodnoty 22 µm na hodnotu 7,5 µm (2. průchod), 4,6 µm (5. průchod), 0,3 µm ( 8. průchod). Deformovaná struktura po žíhání při teplotě 620 C/1 h rekrystalizovala. Po všech průchodech došlo k mírnému nárůstu zrna. Změny tvrdosti po jednotlivými průchodech jsou po tepelném zpracování nevýrazné. Vzrůstající trend tvrdostí s rosucím počtem průchodů je však zachován. Dislokační zpevnění bylo rekrystalizací odbouráno. Závislost velikosti meze kluzu na velikosti zrna odpovídá Hall- Petchovu vztahu. 1. Introduction It is required that a material for dental implants is bio compatible, it must not be xic and it may not cause allergic reactions. It must have high ultimate tensile strength R m and yield strength R p at low density ρ and low modulus of elasticity E. Metallic materials used for dental implants comprise alloys of stainless steels, cobalt alloys, titanium (coarse-grained) and titanium alloys [1, 2]. Semi-products in the form of coarsegrained Ti or Ti alloys are used as bio-material for medical and dental implants since the second half of the sixties of the last century [4]. Titanium is at present preferred stainless steels and cobalt alloys namely thanks its excellent biocompatibility [3-5]. Together with high biocompatibility of Ti its resistance corrosion evaluated by polarisation resistance varies around the value 10 3 R/Ωm [6]. It therefore occupies a dominant position from this viewpoint among materials used for dental implants. In the past years a higher attention was paid also titanium alloys due requirements higher strength properties. The reason was the fact that titanium alloys had higher strength properties in comparison with pure titanium. Typical representative of these alloys is duplex alloy (α a β Ti6Al4V [7-9]. After application of dental implants made of these alloys xicity of vanadium was confirmed. Aluminium, o, can be categorised among potentially xic elements. During the following development of dental implants the efforts were concentrated on replacement of titanium alloys containing xic and potentially xic elements by nonxic elements. That s why new alloys of the type TiTa, TiMo, TiNb and TiZr began be used. Single phase β 51
Ti alloys were developed at the same time, which are characterised by the low value of the modulus of elasticity [10]. Ti alloys with elements with very different density and melting temperature (TiTa, TiMo) require special technology of manufacture, by which they significantly increase production costs and price of semi-products for dental implants. The problem at the development of metallic biomaterials consists not only in their real or potential xicity, but also in their allergenic potential [11]. Sensitivity of population allergies keeps increasing. Allergies metals is caused by metallic ions, which are released from metals by body fluids. Share of individual metals on initiation of allergies is different. What concerns the alloying elements for dental implants special attention is paid namely Ni and Co, as their allergenic effect varies around (13,5%) and Cr (9,5%). Some titanium alloys also contain the elements classified as allergens. These are e.g. the following alloys: Ti13Cu4,5Ni; Ti20Pd5Cr; Ti20Cr0,2Si. Sensitivity of population Ni is increasing. For these reasons pure titanium still remains be a preferred material for dental applications. Development trend in case of this material is oriented on preservation of low value of the modulus of elasticity and on increase of mechanical properties, especially strength. According the Hall-Petch relation it is possible increase considerably strength properties of metals by grain refinement. That s why it is appropriate use for dental implants rather fine-grained Ti instead of coarse-grained Ti. Use of ultra grained concerns has numerous fields including medicine. Bulk ultra grained structural metallic materials are used for dental applications. These are materials with the grain size smaller than approx. 300 nm [12]. High-purity titanium is used for dental implants. 2. Structure and properties of titanium Tab. 1. Chemical analysis of the used commercially pure titanium (CP), (weight %) Tab. 1. Chemické složení použitého titanu 52 O 0.068 C 0.008 Fe 0.03 Al 0.01 Cr 0.01 Tensile strength Rp0,2 Yield strength Elongation Reduction of area [ MPa] 365 [ MPa] 212 [ %] 51 [ %] 71 Tab. 3. Hardness of commercially pure Ti before and after cold rolling. Tab. 3. Počáteční tvrdost titanu a tvrdost po válcování za studena HV30 Label 139 131 130 200 202 194 Sample 1 Sample 2 Sample 3 Commercially pure titanium (CP) bars and sheets were used in this study. The average grain size of the asreceived CP titanium is ASTM no. 4. Tensile specimens with a gauge length of 50 mm, 10 mm width and 3.5 mm thickness were machined with the tensile axis oriented parallel the final rolling direction. The specimens were deformed at room temperature with different initial strain rates. Fig. 1 4 shows microstructure of deformed specimens after testing. The specimens were sectioned along the gauging length and gripping parts of the deformed sample. The samples were then polished and etched using 10 % HF, 10 % HNO3 and 80 % H2O for 20 seconds. Chemical analysis and mechanical properties of titanium are given in the Table 1-3. N 0.004 Tab. 2. Mechanical properties of CP titanium after annealing 649 C/1 hour (ASTM E8) Tab. 2. Mechanické vlastnosti titanu po žíhání 649 C/1h Ti Rest. Fig. 1. Initial microstructure of titanium: Obr. 1. Výchozí mikrostruktura vzorků: podélný směr; příčný směr
cobalt alloys Rm/ρ = 160 (Ν m/g). Disadvantage of dental implants based on steel or cobalt alloys is their high modulus of elasticity: E = 200 240 GPa, while in case of titanium and its alloys this value varies between 80 and 120 GPa [15, 16]. At present only few companies in the world manufacture commercially bulk nano-materials. The technology for manufacture of ultragrained Titanium The main objective of experiments was manufacture of ultra-grained titanium, description and optimisation of its properties from the viewpoint of their biocompability, resistance corrosion, strength and other mechanical properties from the viewpoint of its application in dental implants. Chemical purity of semi products for ultra-grained titanium was ensured by technology of melting in vacuum and by zonal remelting. The obtained semi-product was under defined parameters of forming processed by the ECAP technology. The output was ultra grained titanium with strength of approx.1050 MPa. The obtained ultragrained titanium was further processed by technology of rotation forging and drawing the shape suitable for dental implants. Obtained results and their analysis Fig. 2. Microstructure of titanium after cold rolling: Obr.2. Mikrostruktura titanu po válcování za studena: podélný směr; příčný směr Semi products from individual heats were processed according modified programs by the ECAP technology and then drawn a wire. Wire diameter varied about 4-5 mm [17-19]. ECAP technology and drawing was made in variants: Properties of ultra-grained titanium Ultra-grained titanium is characterised by exceptional mechanical property, among which high ultimate strength and high yield strength are of utmost importance. Strength of ultra-grained titanium must have the following values: Rm > 0 MPa, Rp0.2 > 850 MPa [6]. Apart from the strength, another important property of dental implants is their so called specific strength (strength related density). Mechanical properties of metallic material for implants are evaluated in relation its density as so called specific properties. In case of classical coarse-grained titanium the relation (Rm/ρ) varies around 70 120 (N m/g), for the alloy Ti6Al4V it varies around 200 (N m/g) [13, 14], and for ultra-grained titanium it is possible predict the values Rm/ρ = 270 (Ν m/g). As a matter of interest it is possible give the specific strength also for some other dental materials: steel AISI 316L - Rm/ρ = 65 (Ν m/g), 8 passes ECAP at a temperatures of 280 oc; with annealing between individual passes, c) Rotation re-forging a diameter of 10 mm (cold forming : e = 2.2), d) The following technology of drawing was realised at increased temperatures. The samples for mechanical tests and for microstructural analyses were prepared from individual variants of processing. On the basis of the results, particularly the obtained strength values, several variants were chosen for more detailed investigation of developments occurring in the microstructure at application of the ECAP and subsequent drawing after heat treatment. Structure of ultra-grained titanium after application of the ECAP process is shown in the Figure 5, 6 and 7. The microstructure was analysed apart from light microscopy also by the X-ray diffraction. Table 4 summarises the obtained basic mechanical properties. 53
Tab. 4. Mechanical properties of titanium after ECAP and drawing Tab. 4. Mechanické vlastnosti jemnozrnného titanu po ECAP a tažení Forming process mechanical properties before ECAP ECAP (2 passes) ECAP (8 passes) Drawing (finishing diameter Dd = 6 mm) Rm A E dz [MPa] [%] [GPa] [nm] 377 32.7 82.7 1200 579 14.7 80.1 950 960 12.3 1030 1050 9.4 300 300 Fig. 4. Microstructure of titanium after 8 ECAP passes Obr. 4. Mikrostruktura titanu po 8 průchodech ECAP Conclusion Technology of manufacture of ultra-grained titanium was proposed and experimentally verified. Grain refinement in input materials was obtained using the ECAP process. In conformity with the Hall-Petch relation the strength properties of Ti increased significantly as a result of grain refinement. The obtained mechanical properties correspond with the declared requirements. Ultra-grained titanium has higher specific strength properties than ordinary titanium. Strength of ultra-grained titanium around 1250 MPa, grain size around 300 nm. Acknowledgement The research was supported by the Grant Agency of the Czech Republic by the grant No. 106/09/1598. Literature Fig. 3 Microstructure of ultra-grained titanium after 2 ECAP passes: Obr. 3. Miktrostruktura jemnozrnného titanu po dvou průchodech ECAP: podélný směr; příčný směr 54 [1] MARCINIAK, J.: Biomaterials, Edited by Silesian University of Technology, Gliwice, 2002. [2] GIERZYŇSKIA-DOLNA, M. et al: Titanium and its alloys. Processing and application in technology and medicine, Edited by Czeschowa University of Technology, Czeschowa, 2002. [3] HUNTER, R., ALISTER, F., MŐLLER, J., ALISTER, J.: Journal of Achievements in Materials and Manufacturing Engineering 22 (2007) 1, 77-80. [4] STOYKA, V., KOVAC, F., JULIUS, B.: Metalurgija, 48 (2009) 2, 99-102. [5] KRUPA, D., BASZKIEWICZ, J.., SOBCZAK, J., BILINSK, A., BARCZ, A.: Journal of Materials Processing Technology, 143144 (2003) 158-163. [6] FAJFAR, P.: Metalurgija, 45 (2006) 3, 239-241. [7] KIERZKOWSKA, A., KRASICKA-CYDZIK, E., JENEK, M.: Biomaterials Engineering, 47-53 (2005), 146-148. [8] ŽITŇANSKÝ, M., ČAPLOVIČ, L., GREGER, M.: Proceedings of the 10th Scientific International Conference Achievements in Mechanical and Materials Engineering AMME 2002, Gliwice Zakopane, 2002, 631-636. [9] TAN, M. J., ZHU, X. J.: Journal of Achievements and Manufacturing Engineering, 18, 1-2 (2006), 183-186. [10] KURODA, D., NIINOMI, M., MORINAGA, M., KATO, Y., YASHIRO, T.: Materials Science and Engineering, Vol. 243 (1998), 1-2, 244-249.
[11] BARON, A., SZEWIECZEK, D., NOWOSIELSKI, R.: Journal of Achievements in Materials and Manufacturing Engineering, 20 (2007) 1-2, 83-86. [12] ZRNÍK, J., MAMUZIĆ, I., DOBATKIN, S. V., STEJSKAL, Z., KRAUS, L.: Metallurgia, 46 (2007) 1, 21-27. [13] DOBATKIN, S. V., ZRNÍK, J., MAMUZIĆ, I.: Metalurgija, 45 (2006) 4, 313-321. [14] ŽITŇANSKY, M., ČAPLOVIČ, L., REHÁK, L., MAKAI, F.: Journal of Achievements in Materials and Manufacturing Engineering, 24 (2007) 1, 146-152. [15] ADAMUS, J.: Archives of Materials Science and Engineering, 28 (2007) 5, 313-316. [16] ZRNÍK, J., MAMUZIĆ, I., DOBATKIN, S. V.: Metalurgija, 45 (2006) 4, 323-331. [17] GREGER, M., KOCICH, R., ČÍŽEK, L., DOBRZANSKI, L. A., WIDOMSKÁ, M.: Science and Engineering, 28 (2007), 709-716. [18] KANDER, L., GREGER, M. : Fatigue Properties of AISI 316 Grade Steel after ECAP Technology, Proceedings of 17 th European Conference on Fracture Multilevel Approach Fracture of Materials, Components and Structures. VUTIUM, Brno 2008, 2429-2436. [19] GREGER, M., KOCICH, R., ČÍŽEK, L. et al: A. : Journal of Achievements in Materials and Manufacturing Engineering, 18 (2006), 1-2, 103-106. Recenze: Prof. Ing. Ladislav Pešek, CSc. Kurzarbeit má spasit zaměstnance Lidové noviny 28.7.2009 Odbory od vlády i zaměstnavatelů vehementně žádají zavést zkrácený pracovní týden. Od podzimu tiž věští prudký nárůst nezaměstnanosti. Začne stát masově dovat firmám výdaje na mzdy? Odbory nevylučují, že nezaměstnanost v ČR supne během podzimu až na 10 % a v některých regionech, jako například v severních Čechách, může zůstat bez práce každý pátý člověk. Negativní vývoj v mnoha firmách s mizivým množstvím zakázek, nedostatkem likvidity a čas i přesunem výroby do jiných zemí skutečně představuje vážnou hrozbu, varuje předseda odborového hnutí Kovo Josef Středula. Odboráři pro chtějí, aby firmy ve velkém zavedly po vzoru Německa zkrácený pracovní týden, tzv. kurzarbeit, a aby stát doval firmám výdaje na mzdy v době, kdy zaměstnanci budou na nucené dovolené. Nyní může zaměstnanec pobírat od firmy 60 % platu v době, kdy má nucené volno. Podle našich požadavků by měl pobírat až 80 % základního platu s tím, že dvacetiprocentní navýšení by doval stát, vysvětlil Středula. Odboráři ten požadavek už naslili na jednání tripartity v červnu. Ministerstvo práce a sociálních věcí připouští, že mzdy je možné dovat v případě, že umožní legislativa (mj. pravidla pro poskyvání veřejné podpory) a finanční prostředky ve státním rozpočtu. Středula argumentuje tím, že dováním zkrácené pracovní doby by stát nezchudl. Ušetřil by prý na dávkách nezaměstnaným a také by zabránil podvodným praktikám firem, které aby nemusely platit sociální a zdravotní pojištění rozvazují se zaměstnanci pracovní poměr a poté je najímají např. formou dohody o provedení práce. Děkan národohospodářské fakulty Vysoké školy ekonomické v Praze Jiří Schwarz upozornil, že dování mezd firmám by pravděpodobně naplňovalo znaky nepovolené podpory firmám, kterou legislativa EU zakazuje. Kdyby měly navíc všechny firmy na takové dotace nárok, došlo by ke kolapsu státního rozpočtu. Někteří zaměstnavatelé, např. ArcelorMittal Ostrava či aumobilka Škoda Au, se k návrhu zkrácených pracovních týdnů staví kladně. Škoda Au uvažuje o jejich zavedení od roku 2010. SB Stát prodal za sedm miliard akcie ArcelorMittal Ostrava tyden.cz 28.7.2009 Hutní společnost ArcelorMittal v rámci dohody o narovnání s Českou republikou již převedla 1 mld. Kč za 11procentní státní podíl ve firmě ArcelorMittal Ostrava. Zbylých 6 mld. Kč by měl podnik převést ve splátkách do státní pokladny do roku 2015. Převod akcií byl podmíněn definitivním uzavřením arbitráže mezi ČR a společností ArcelorMittal, která byla ukončena v červnu 2009. Kupní cena za jednu akcii činí 5 000 Kč, což v celkovém objemu představuje téměř 7 mld. Kč. Vzhledem k mu, že cena za akcii byla znalcem stanovena v roce 2008 a k podpisu dohod došlo až v roce 2009, souhlasilo ministerstvo financí s rozložením plateb do sedmi splátek. Cena akcií od loňského roku výrazně klesla. Cena akcií je v současnosti ve výši dvou pětin ceny dohodnuté v roce 2008. Transakce je pro pro stát velmi výhodná, a i vzhledem k současné hospodářské situaci a situaci ve firmě. Platba je rozložena do splátek. Do doby splacení má ministerstvo financí na všechny prodávané akcie zástavní právo, což řeší případ, že by firma splátky nedodržela. SB 55