1 TENKÉ VRSTVY NA ŘEZNÝCH NÁSTROJÍCH V APLIKACI OBRÁBĚNÍ PLASTŮ THIN FILM-COATED CUTTING TOOLS FOR CUTTING OF PLASTICS Antonín Kříž a) Pavel Kožmín b) Department of Material Engineering and Engineering Metallurgy, ZČU-Plzeň, Univerzitní 22, Plzeň , Czech Republic Hofmeister s.r.o., Mezi Ploty 12, Plzeň, Czech Republic Abstrakt There are widespread applications of thin films in the field of cutting tools. It is their use which currently expands machinability limits into previously hard-to-machine materials. One of such examples is cutting of glass fibre reinforced plastics. Not only thermal load but also abrasive and adhesive stresses act upon such tools. In order to stand combined loads of this type, the tools must be coated with high-quality thin films, which meet strictest requirements. Of no less importance are properties and surface state of substrate, including its geometry. This is the focus of the present paper, which gives a summary of achieved results. It comprises literature search data, experimental results and practical experience. As shown further, resistance to such diverse loads may be obtained only in such tools, in which such problems had been treated in a complex manner. This is the reason for extensive experiments covering not only thin films and substrates but also tool manufacture and application. Wear on the tool has been examined by scanning electron microscope and by extensive laboratory tests. Relationships between the results suggest the solution for the use of thin films for cutting tools for said composite hard-to-machine materials. Tenké vrstvy našly velmi široké uplatnění v oblasti řezných nástrojů. V současné době posouvají hranici obrobitelnosti do oblasti dříve těžkoobrobitelných materiálů. Takovým příkladem je i obrábění plastů vyztužených skelným vláknem. Nástroj je namáhán nejen tepelně, ale i abrazivně a adhezivně. Takovémuto kombinovanému namáhání může obstát pouze nástroj, který je opatřen kvalitní povrchovou tenkou vrstvou, která splňuje ta nejvyšší kritéria. Důležité jsou i vlastnosti substrátu (vlastní nástroj) a stav jeho povrchu, včetně geometrie. Touto problematikou se zabývá příspěvek, který shrnuje dosažené výsledky, získané nejen z rešeršní činnosti, ale především i z vlastních experimentů a praktických zkušeností. Jak bude presentováno, nástroj může odolat tak různorodému opotřebení, pouze tehdy, když je tato problematika komplexně řešena. Z tohoto důvodu jsou dělány rozsáhlé experimenty nejen u tenkých vrstev a substrátu, ale i v procesu zhotovování nástrojů a následně i při jejich aplikaci. Opotřebení nástroje je vyhodnoceno pomocí řádkovacího elektronového mikroskopu a je doplněno i poznatky z rozsáhlých laboratorních testů. Ze vzájemné korekce výsledků vyplývá řešení a aplikace tenkých vrstev na nástroje pro obrábění uvedených kompozitních, těžkoobrobitelných materiálů. 1
2 1. ÚVOD Definovat těžkoobrobitelný materiál je velice obtížné a závisí to na komplexním chování obráběného materiálu při obrábění řeznými nástroji. Následkem kontaktu mezi nástrojem-obrobkem a nástrojem-třískou dochází k opotřebení nástroje. Tento proces je velmi složitý a závisí na mnoha faktorech (fyzikálních a zejména mechanických vlastnostech obráběného a nástrojového materiálu, druhu obráběcí operace, geometrii nástroje, pracovních podmínkách, řezné prostředí, atd.). V průběhu opotřebení působí mnoho odlišných fyzikálně-chemických jevů, které mají dynamickou povahu tj. nejsou časově konstantní. Jak bude v tomto článku zachyceno, i speciální polymerní materiály vyztužené skleněným vláknem spadají do této kategorie Mechanismy opotřebení U velmi tvrdých materiálů je dominantní abraze, která je charakteristická postupným odbrušováním břitu. K tomuto mechanismu se může připojit vydrolování břitu, které je způsobeno výskytem tvrdších částic v řezu než má samotný břit. To má za následek intenzivní namáhání břitu a dochází tak k jeho předčasné destrukci. U měkkých materiálů převažuje adheze, která je spojena s nalepováním materiálu na břit a jeho postupným vylamováním. V tomto případě se může vyskytovat i chemické opotřebení, které je způsobeno chemickou reakcí mezi obrobkem a nástrojem. Abraze a adheze jsou též obvykle označovány jako fyzikální mechanismy opotřebení, difúze a oxidace pak jako opotřebení chemické. Mnohdy tyto mechanismy působí komplexně, kdy se pouze mění jejich důležitost v procesu opotřebení. Schopnost břitu odolávat abrazivnímu otěru je z větší části závislá na jeho tvrdosti. Řezný materiál, který obsahuje hustou strukturu tvrdých částic, bude abrazivnímu otěru odolávat dobře, avšak nemusí stejně dobře odolávat také jiným mechanismům opotřebení. Adhezní otěr se vyskytuje hlavně při nízkých teplotách obrábění na čele břitu nástroje. Je významný při nižších řezných rychlostech, kdy vzniká bodový styk mezi třískou a nástrojem a kdy je umožněno adhezní spojení obou materiálů Odolnost proti opotřebení u řezných nástrojů V minulosti se na tyto potřeby reagovalo vývojem nových materiálů, z nichž byl nástroj vyroben. Důkazem toho je vývoj rychlořezných ocelí (RO), jejichž vývoj počíná kolem roku 1900, kdy F.W. Taylor formuloval na základě výsledků svých prací chemické složení první, dnes již známé RO typu 18%W, 4%Cr, 1%V (ČSN ), která si své významné postavení zachovává dodnes.v roce 1930 se objevuje rychlořezná ocel s přísadou kobaltu od 3 do 5%[1]. Další vývoj směřoval do vytváření speciálních strukturních fází založené na přítomnosti komplexních karbidů. Vedle tohoto rozvoje se začaly využívat další poznatky, které vedly k výrobě nástrojů ze slinutých karbidů. Počátky výroby nástrojů ze slinutých karbidů sahají do období před II. světovou válkou, která ještě urychlila jejich vývoj, ačkoliv chyběly strategické suroviny. Z tehdejší doby se zachovalo označení WIDIA pro vrtáky osazené plátky ze slinutých karbidů. Toto označení vzniklo na základě dosažení vysoké tvrdosti WIe DIAmant jako diamant)[2]. V 50. letech pokračuje silný vývoj SK materiálů právě v oblasti řezných nástrojů, kdy se začínají uplatňovat jemnozrnné struktury, jejichž masové nasazení je již na konci šedesátých let. V dnešní době se nástroje ze slinutých karbidů aplikují především v oblastech, kde se zpracovává tzv. těžkoobrobitelný materiál. Dalším materiálem používaným velmi často v oblasti těžkoobrobitelných materiálů jsou cermety. Jejich název vznikl složením z CERamics-METal. Na rozdíl od Sk materiálů jsou zde použity tvrdé fáze TiC+TiN. Jako pojivo se používá především nikl, ale jsou zastoupeny 2
3 i další kovy, titan, kobalt popř. molybden. Vývoj těchto materiálů se odehrává především v Japonsku a v USA. V současné době se již cermetové nástroje aplikují i v zemích EU. Dalším materiálem, který v současné době dosahuje značného významu, je řezná keramika. Řezná keramika patří mezi anorganické, nekovové převážně krystalické materiály. Podle chemického složení se dělí do dvou základních skupin, a to na oxidickou a neoxidickou řeznou keramiku. Historický vývoj tohoto materiálu byl velmi složitý, přestože keramika byla aplikována na první nástroj, který používal člověk již v době kamenné. V novodobé historii se však průmyslové aplikace datují až do oblasti 40. let minulého století. Plné využití předností řezné keramiky je však stále ještě budoucností. Přesto již v současné době je použitím řezné keramiky řešena celá řada problémů s těžkoobrobitelnými materiály a to především tam, kde je plynulý řez s minimálním chvěním a rázy[3]. Uvedené materiály, v současné době, velmi omezeně splňují komplexní vlastnosti, které jsou na ně kladeny v souvislosti s novými progresivními způsoby obrábění. Je to především obrábění materiálů s vyšší pevností nebo naopak vyšší plasticitou, materiálů sendvičových nebo kompozitních a v neposlední řadě i obrábění s vyšší rychlostí se snahou eliminovat přítomnost procesních kapalin. Vyvinout objemový materiál, který by splňoval tyto komplexní vlastnosti není možné, proto se tato situace řeší aplikací tenkých vrstev na bázi nitridů popř. karbidů i oxidů kovů. Ty svými vlastnostmi jako je vysoká tvrdost, odolnost proti otěru, oxidaci, korozi i za vyšší teploty, nízkým součinitelem tření, působí proti účinku různých mechanismů opotřebení. Vlastnosti a zejména chování nástrojů s tenkými vrstvami v provozu jsou závislé na mnoha činitelích. Z hlediska vlivu tenké vrstvy jsou podstatným faktorem fyzikální vlastnosti tenké vrstvy dané způsobem depozice tenké vrstvy a podmínkami, za jakých k depozici dochází. Vlastní materiál řezného nástroje působí svými fyzikálními vlastnostmi podmíněnými jeho chemickým složením, technologickým zpracováním a tvarovým provedením. Nelze opomenout řezné podmínky, za kterých břit nástroje pracuje, a které se velmi výrazně promítají do chování řezného nástroje. Jak dokumentuje obr.č.1 depozicí tenké vrstvy dochází k posunu směrem k tzv. ideálnímu řeznému materiálu. Obr. 1 Vliv depozice tenké vrstvy na zlepšení užitných vlastností nástroje Fig.1 - Enhancement of end-use properties of the tool by thin film coating. Tenká vrstva spolu s materiálem řezného nástroje vytváří neodlučitelný systém, jehož vlastnosti závisí na celé řadě dalších faktorů (obr.2). Proto je třeba hledat cestu ke zlepšení užitných vlastností tohoto systému komplexně. Sledovat nejen stav materiálu řezného nástroje (používá se terminologie substrát), ale i jeho geometrii, kvalitu nabroušení a povrchový stav, který je spojen s předdepozičním i depozičním procesem. Vedle těchto materiálových faktorů mají důležitou roli i technologické podmínky použití nástroje a další vnější aspekty jako např. tuhost soustavy stroj-nástroj-obrobek. Tento přístup je aplikován i v následujícím praktickém případě. 3
4 Otěruvzdorná vrstva Odolnost proti opotřebení Redukce tření Korozní odolnost Difúzní bariéra Tepelná bariéra Mezivrstva Adheze Bariéra rozvoje trhlin Kompenzace diletace a pnutí Modifikace struktury a morfologie Substrát Pevnost Tuhost Geometrie Obr. 2 Skladba a jednotlivé funkce systému tenká vrstva-substrát Fig.2 - Structure and individual functions of the thin film-substrate system 2. OBRÁBĚNÍ PLASTŮ Při obrábění plastů je nutné počítat se špatnou tepelnou vodivostí a relativně nízkým bodem tání plastů. Proto je třeba zajistit, aby vzniklé teplo bylo udržováno na nejnižší možné úrovni s co nejmenším přechodem na obráběné součásti. Zabrání se tak změnám v barvě a tání povrchu plastů. Z tohoto důvodu je nutné dodržet následující doporučení: - nástroj musí být udržován neustále ostrý a hladký - nástroj musí mít takový tvar, aby se obráběného materiálu dotýkal jen řeznou plochou - při operacích, kdy vzniká nadměrné teplo (např. při vrtání), je vhodné použít chladící médium Jako materiál pro řezný nástroj se používají běžné materiály pro kovoobrábění. Pro svou dlouhodobou trvanlivost jsou však nástroje s břitem ze slinutého karbidu lepší než nástroje z rychlořezné oceli. Platí to zejména při obrábění grafitu, MoS 2 a termoplastů vyztužených skelným vláknem, kde adhezivnímu účinku přistupuje ještě značná abraze, vzniklá díky přítomnosti tvrdých částic vzniklých z těchto vláken. U plastů vyztužených skelným vláknem je hlavní problém ve zmíněné kombinaci mechanismu opotřebení, důležitým hlediskem je směr vlákna ke směru obrábění. To má za následek, že při nevhodně zvoleném úhlu vláken a posuvu nástroje dochází k vytrhávání a praskání základní matrice materiálu okolo vláken. Z rozsáhlé rešeršní práce, která byla provedena v rámci řešení projektu MPO byly zjištěny následující závěry: Ačkoliv je problematika obrábění plastů vyztužených skleněnými vlákny velmi aktuální, věnuje se tomuto směru velmi málo odborníků i výrobních firem. Jednoznačně byl potvrzen trend v použití nástrojů vyrobených ze slinutých karbidů opatřených otěruvzdornými tenkými vrstvami. Tyto vrstvy mohou být jak na bázi nitridů kovů, tak i progresivní diamantové vrstvy. 4
5 Významnou pozornost si zaslouží i stav nástroje před depozicí a to nejen z hlediska geometrie, ale i z hlediska stavu břitu v mikrorozměrech. Další pozornost je také třeba věnovat samotnému procesu obrábění a vzniku a rozvoji poškození. Tyto rešeršní zkušenosti byly využity nejen při přípravě následujícího experimentu. 3. PRAKTICKÉ ZKUŠENOSTI Z OBRÁBĚNÍ PLASTŮ K experimentu byl použit v praxi aplikovaný polymerní materiál skládající se z několika částí. Jak dokumentuje obr. 3 obráběný kompozit obsahuje vedle polypropylenu vyztuženého skleněným vláknem i velmi měkký materiál polyuretanovou pěnu a měkčenou polyuretanovou fólii. Polypropylen je vyztužen vlákny, které jsou v rozmístěny v různých směrech a v různé heterogenitě. Místy je obsah skleněných vláken o průměrné délce 12 mm až 50%. Z tohoto důvodu jsou výsledky obrábění ovlivněny Obr. 3 Skladba obráběného kompozitu Obr. 4 Vzhled vyztužujícího vlákna po shoření polypropylenové matrice Fig Appearance of the reinforcing fibre upon polypropylene matrix burning Fig. 3 - Structured of the machined composite material heterogenitou obrobku a pro správné podchycení vlivu jednotlivých faktorů je nutné provádět rozsáhlé a statisticky vyhodnocované zkoušky trvanlivosti ostří. Na materiál této skladby je třeba pohlížet jako na kompozit a to jak z hlediska jeho mechanických vlastností, tak i opotřebení, které vzniká na nástroji při obrábění. Skleněná vlákna iniciují silné abrazivní poškození a měkký polypropylen s izolačními vlastnostmi vyvolává adhezivní degradaci břitu nástroje. Adhezní mechanismus má za následek nejen poškození břitu, ale i změnu geometrie nástroje, která s sebou přináší změnu řezných podmínek. Podmínkou úspěchu je použití kvalitního slinutého karbidu, jehož výběr byl podřízen předpokládanému namáhání břitu. Z čehož plynou vysoké požadavky na tvrdost materiálu a oproti tomu však je nebezpečí nižší houževnatosti a elasticko-plastických charakteristik materiálu. Volbě materiálu byla věnována vysoká pozornost, o čemž svědčí řada provedených zkoušek, které byly součástí stanovování rozhodujících vstupních podmínek. Struktura slinutého karbidu je zachycena na obr.č. 5. Obrazovou analýzou byla zjištěna průměrná velikost karbidického zrna WC (karbid wolframu) 0,5 µm. Tímto rozměrem je tento slinutý karbid zařazen do kategorie velmi jemných materiálů ( ULTRAFEIN ). 5
6 Obr. 5 - Struktura slinutého karbidu. Z obrazové analýzy provedené na velkém množství snímků při zvětšení x pořízených pomocí elektronového řádkovacího mikroskopu byla stanovena velikost karbidického zrna. Fig. 5 -Structure of the sintered carbide. The carbide grain size was determined by image analysis from vast number of scanning electron micrographs taken at 10,000 magnification. Významnou charakterizující veličinou dokumentující nejen chemické složení, ale i velikost zrna je tvrdost materiálu. Z tohoto důvodu bylo provedeno stanovení tvrdosti normovanou zkouškou dle Vickerse a to při zatížení 490,5 N (HV50). Z rozměrů iniciovaných trhlin od proniknutí Vickersova jehlanu byla stanovena hodnota lomové houževnatosti K IC, která je uvedena spolu s příslušnou tvrdostí. Jak vyplývá z následujícího vztahu, pro výpočet lze použít pouze ztížení odpovídající HV50. K IC = 6,2 HV50 L MPa m Tvrdost vybraného slinutého karbidu dosahovala hodnoty HV50=1710. Z rozměru iniciovaných trhlinek byla dle uvedeného vztahu spočtena lomová houževnatost K IC = 10,2 MPa m 1/2. Zkoušky trvanlivosti byly prováděny při následujících řezných podmínkách: v c minim = 400m/min; f z minim = 0,01 mm/zub; a p = 5 15 mm; bez chlazení Na nástroje jednobřité frézy byla deponována vrstva TiAlN. Některé nástroje byly vedle této vrstvy opatřeny povrchovou kluznou vrstvou. Pro stanovení velikosti opotřebení a tím životnosti nástroje byly v rámci technické přípravy zkoumány tzv. standardní (běžně užívané nástroje). Následující snímky dokumentují kvalitu obráběné plochy a mechanismus poškození nástroje. V některých případech se vyskytlo lokální vyštípnutí nástroje, které může být iniciováno z následujících důvodů: 1) nástroj se dostal do oblasti s větším výskytem zpevněných skleněných vláken, 2) bylo iniciováno větší chvění v důsledku uchycení obrobku, polohy nástroje nebo změny řezných podmínek (změna geometrie, výkon stroje atd.), 3) opotřebení a vnitřní pnutí v nástroji dosáhlo takové úrovně, že vyvolalo jeho lokální poškození, 4) vadou v základním materiálu (substrátu slinutý karbid, popř. defektní povrchová vrstva). Jak vyplývá z uvedených hodnot v tabulce 1, pak tento proces poměrně rychlé degradace nástroje nastal v několika případech, v jednom nastala úplná destrukce celého nástroje. 1/2 6
7 Obr. 6 - Zhoršená kvalita obrobené plochy je odrazem stavu nástroje Fig.6 - Poor quality of the machined surface reflects the condition of the tool Obr. 7 - Břit nástroje v pohledu od hřbetu vykazuje minimální příznaky poškození, přesto kvalita jím obrobené plochy byla klasifikována jako nepřípustná. Fig. 7 - Cutting edge of tool viewed from the tool flank shows only minor traces of wear. Despite, the quality of the surface machined with this tool was rated as unacceptable Uvedený nástroj obrobil pouze 20 dílů a pak musel být pro podstatné zhoršení obrobené plochy vyřazen. Následující tabulka 1 zachycuje množství obrobených kusů v souvislosti s použitou povrchovou vrstvou. Nástroj Počet kusů Příčina výměny TiAlN 431 Zlomený nástroj TiAlN 7 Zlomená špička TiAlN 5 Zlomená špička TiAlN 9 Zlomená špička TiAlN 280 Opotřebený nástroj TiAlN 66 Opotřebený nástroj TiAlN 168 Opotřebený nástroj TiAlN 99 Opotřebený nástroj TiAlN 7 Opotřebený nástroj TiAlN+C vrstva 15 Opotřebený nástroj TiAlN +C vrstva 121 Opotřebený nástroj TiAlN +C vrstva 348 Opotřebený nástroj TiAlN +C vrstva 46 Opotřebený nástroj Tabulka 1 Počet dílů obrobených jednotlivými nástroji Table 1 - Proportions of parts machined with different tools 7
8 4. ZÁVĚR Jak vyplývá z uvedených výsledků, je aplikace obráběná plastů vyztužených skleněnými vlákny se sendvičovým řešením s dalšími polypropyleny na samém začátku zájmu. Tato situace není v zahraničí nikterak lepší, spíše naopak. Stále převládá názor, že pro tuto aplikaci jsou vhodné nástroje bez povrchové vrstvy a mnohdy se dokonce používají nástroje z rychlořezné oceli. Jak vyplývá z uvedených experimentů, dosahuje se zde, oproti klasickým řezným procesům, zcela jiného mechanismu poškození a to především z hlediska jeho rozsahu. Nástroj, který je poškozen v řádu několika mikrometrů vykazuje nevhodné podmínky pro další použití a to následkem výrazně zhoršené plochy obrobku. Experimenty jsou teprve na samém počátku zkoumání, ale již teď je zřejmé, že daný problém bude muset být řešen komplexně a to jak z pohledu vhodného slinutého karbidu, tak i vhodné geometrie a stavu povrchu. Stav povrchu, jak z hlediska broušení, tak i povrchových vrstev bude mít velký vliv na dosažené výsledky. Další plánovaný vývoj rozvoje těchto nástrojů půjde tímto směrem. Vedle zmíněných změn geometrie, materiálu nástroje a povrchové vrstvy je plánován i experiment, kdy se bude pomocí předdepozičních procesů měnit stav a geometrie nástroje v mikrorozměrech. Tyto změny by měly iniciovat vyšší kvalitu řezné hrany a tím i delší trvanlivost nástroje. Tento příspěvek je možné stáhnout na internetové stránce Tento příspěvek vznikl na základě řešení projektu MPO - FI-IM2/054. LITERATURA [1] FREMUNT, P.: Nástrojové oceli. 1. vyd.brno s. [2] BROOKES, K.J.A.: World Direktory and Handbook of Hardmetals. East Barnet Herts, United Kingdom, International Karbide 1987, 5th edition, s [3] TAKATSU, S.: Recent deveopments in hard cutting tool materiále. High Temperature Materiále and Processes, Vol , 1990, s
TENKÉ VRSTVY NA ŘEZNÝCH NÁSTROJÍCH PRO TĚŽKOOBROBITELNÉ PLASTY THIN FILM-COATED CUTTING TOOLS FOR HARD-TO-MACHINE PLASTICS
TENKÉ VRSTVY NA ŘEZNÝCH NÁSTROJÍCH PRO TĚŽKOOBROBITELNÉ PLASTY THIN FILM-COATED CUTTING TOOLS FOR HARD-TO-MACHINE PLASTICS Antonín Kříž a) Pavel Kožmín b) a) Department of Material Engineering and Engineering
VíceVývoj - grafické znázornění
Poznámka: tyto materiály slouží pouze pro opakování STT žáků SPŠ Na Třebešíně, Praha 10; s platností do r. 2016 v návaznosti na platnost norem. Zákaz šíření a modifikace těchto materiálů. Děkuji Ing. D.
VíceOPOTŘEBENÍ A TRVANLIVOST NÁSTROJE
Poznámka: tyto materiály slouží pouze pro opakování STT žáků SPŠ Na Třebešíně, Praha 10; s platností do r. 2016 v návaznosti na platnost norem. Zákaz šíření a modifikace těchto materiálů. Děkuji Ing. D.
VíceVLIV MIKROSTRUKTURY SLINUTÝCH KARBIDŮ NA ŽIVOTNOST NÁSTROJŮ A STROJNÍCH SOUČÁSTÍ
Sborník str. 363-370 VLIV MIKROSTRUKTURY SLINUTÝCH KARBIDŮ NA ŽIVOTNOST NÁSTROJŮ A STROJNÍCH SOUČÁSTÍ Antonín Kříž Západočeská univerzita, Univerzitní 22, 306 14, Prášková metalurgie - progresivní technologie
VíceNÁSTROJ NEFUNGUJE, KDO ZA TO MŮŽE?
NÁSTROJ NEFUNGUJE, KDO ZA TO MŮŽE? Příspěvek je ve sborníku na str. 67-72, přednáška na www.ateam.zcu.cz Antonín Kříž 3/37 4/37 Čas jsou peníze Systém tenká vrstva-substrát Vrstva Rozhraní Substrát Deponované
VíceVLIV ZPŮSOBŮ OHŘEVU NA TEPLOTNÍ DEGRADACI TENKÝCH OTĚRUVZDORNÝCH PVD VRSTEV ZJIŠŤOVANÝCH POMOCÍ VYBRANÝCH METOD
23. 25.11.2010, Jihlava, Česká republika VLIV ZPŮSOBŮ OHŘEVU NA TEPLOTNÍ DEGRADACI TENKÝCH OTĚRUVZDORNÝCH PVD VRSTEV ZJIŠŤOVANÝCH POMOCÍ VYBRANÝCH METOD Ing.Petr Beneš Ph.D. Doc.Dr.Ing. Antonín Kříž Katedra
VíceVrstvy a povlaky 2007
Vrstvy a povlaky 2007 VLIV MECHANICKÝCH ÚPRAV SUBSTRÁTU TU NA ADHEZI TENKÝCH VRSTEV Martina Sosnová Antonín Kříž ZČU v Plzni Úvod Povrchové inženýrství je relativně mladým vědním oborem. Fascinace člověka
VíceKeramika spolu s dřevem, kostmi, kůží a kameny patřila mezi první materiály, které pravěký člověk zpracovával.
Keramika Keramika spolu s dřevem, kostmi, kůží a kameny patřila mezi první materiály, které pravěký člověk zpracovával. Chceme li definovat pojem keramika, můžeme říci, že je to materiál převážně krystalický,
VíceKatedra obrábění a montáže, TU v Liberci při obrábění podklad pro výuku předmětu TECHNOLOGIE III - OBRÁBĚNÍ je při obrábění ovlivněna řadou parametrů řezného procesu, zejména řeznými podmínkami, geometrií
VíceVÝROBA ŘEZNÝCH NÁSTROJŮ S OTĚRUVZDORNÝMI TENKÝMI VRSTVAMI
VÝROBA ŘEZNÝCH NÁSTROJŮ S OTĚRUVZDORNÝMI TENKÝMI VRSTVAMI Ing. Josef Fajt, CSc. PILSEN TOOLS s.r.o., Tylova 57, 316 00 Plzeň, tel.: +420 378 134 005, e-mail: fajt@pilsentools.cz ANNOTATION The paper is
VíceCENTRUM VZDĚLÁVÁNÍ PEDAGOGŮ ODBORNÝCH ŠKOL
Projekt: CENTRUM VZDĚLÁVÁNÍ PEDAGOGŮ ODBORNÝCH ŠKOL Kurz: Technologie třískového obrábění 1 Obsah Technologie třískového obrábění... 3 Obrábění korozivzdorných ocelí... 4 Obrábění litiny... 5 Obrábění
VíceNÁSTROJ NEFUNGUJE, KDO ZA TO MŮŽE?
NÁSTROJ NEFUNGUJE, KDO ZA TO MŮŽE? Vstupní přednáška pro problematiku: Nástrojové oceli Slinuté karbidy Depozice tenkých vrstev Předmět SMA Doc.Dr.Ing. Antonín Kříž 3/37 Čas jsou peníze 4/37 Systém tenká
VíceSYSTÉM TENKÁ VRSTVA SUBSTRÁT V APLIKACI NA ŘEZNÝCH NÁSTROJÍCH
Západočeská univerzita v Plzni SYSTÉM TENKÁ VRSTVA SUBSTRÁT V APLIKACI NA ŘEZNÝCH NÁSTROJÍCH Antonín Kříž Univerzitní 22, 306 14 Plzeň, e-mail: kriz@kmm.zcu.cz Tento příspěvek vznikl na základě řešení
VíceKroková hodnocení kombinovaného namáhání systémů s tenkými vrstvami. Roman Reindl, Ivo Štěpánek, Radek Poskočil, Jiří Hána
Kroková hodnocení kombinovaného namáhání systémů s tenkými vrstvami Step by Step Analysis of Combination Stress of Systems with Thin Films Roman Reindl, Ivo Štěpánek, Radek Poskočil, Jiří Hána Západočeská
VíceMetalografie. Praktické příklady z materiálových expertíz. 4. cvičení
Metalografie Praktické příklady z materiálových expertíz 4. cvičení Příprava metalografických výbrusů Odběr vzorků nesmí dojít k změně struktury (deformace, ohřev) světelný mikroskop pro dosažení požadovaných
VíceACOUSTIC EMISSION SIGNAL USED FOR EVALUATION OF FAILURES FROM SCRATCH INDENTATION
AKUSTICKÁ EMISE VYUŽÍVANÁ PŘI HODNOCENÍ PORUŠENÍ Z VRYPOVÉ INDENTACE ACOUSTIC EMISSION SIGNAL USED FOR EVALUATION OF FAILURES FROM SCRATCH INDENTATION Petr Jiřík, Ivo Štěpánek Západočeská univerzita v
VíceMOŢNOSTI ZVYŠOVÁNÍ TRVANLIVOSTI NÁSTROJŮ U VÝROBCE OPTIONS OF TOOL LIFE RAISING BY THE MANUFACTURER. Ing. Josef Fajt, CSc., Dr. ing.
Abstrakt MOŢNOSTI ZVYŠOVÁNÍ TRVANLIVOSTI NÁSTROJŮ U VÝROBCE OPTIONS OF TOOL LIFE RAISING BY THE MANUFACTURER Ing. Josef Fajt, CSc., Dr. ing. Miloslav Kesl PILSEN TOOLS s.r.o., Tylova 57, 316 00 Plzeň,
VíceHODNOCENÍ HLOUBKOVÝCH PROFILŮ MECHANICKÉHO CHOVÁNÍ POLYMERNÍCH MATERIÁLŮ POMOCÍ NANOINDENTACE
HODNOCENÍ HLOUBKOVÝCH PROFILŮ MECHANICKÉHO CHOVÁNÍ POLYMERNÍCH MATERIÁLŮ POMOCÍ NANOINDENTACE EVALUATION OF DEPTH PROFILE OF MECHANICAL BEHAVIOUR OF POLYMER MATERIALS BY NANOINDENTATION Marek Tengler,
VícePRASKÁNÍ VRTÁKŮ PO TEPELNÉM ZPRACOVÁNÍ Antonín Kříž
Vakuové tepelné zpracování a tepelné zpracování nástrojů 22. - 23.11. 2011 - Jihlava PRASKÁNÍ VRTÁKŮ PO TEPELNÉM ZPRACOVÁNÍ Antonín Kříž Západočeská univerzita v Plzni Fakulta strojní Katedra materiálu
VíceAntonín Kříž a) Miloslav Chlan b)
OVLIVNĚNÍ KVALITY GALVANICKÉ VRSTVY AUTOMOBILOVÉHO KLÍČE VÝCHOZÍ STRUKTUROU MATERIÁLU INFLUENCE OF INITIAL MICROSTRUCTURE OF A CAR KEY MATERIAL ON THE ELECTROPLATED LAYER QUALITY Antonín Kříž a) Miloslav
VíceVLIV MECHANICKÉHO PORUŠENÍ NA CHOVÁNÍ POVRCHU S TIN VRSTVOU PŘI TEPELNÉM A KOROZNÍM NAMÁHÁNÍ. Roman Reindl, Ivo Štěpánek, Martin Hrdý, Klára Jačková
VLIV MECHANICKÉHO PORUŠENÍ NA CHOVÁNÍ POVRCHU S TIN VRSTVOU PŘI TEPELNÉM A KOROZNÍM NAMÁHÁNÍ Roman Reindl, Ivo Štěpánek, Martin Hrdý, Klára Jačková Západočeská univerzita v Plzni, Univerzitní 22, 306 14
VícePRODUKTIVNÍ OBRÁBĚNÍ OCELI P91
PRODUKTIVNÍ OBRÁBĚNÍ OCELI P91 Ing. Jan Řehoř, Ph.D. Ing. Tomáš Nikl ZČU v Plzni Fakulta strojní, Katedra technologie obrábění ZČU v Plzni, Univerzitní 22, Plzeň e-mail: rehor4@kto.zcu.cz Abstract The
Více8. Třískové obrábění
8. Třískové obrábění Třískovým obráběním rozumíme výrobu strojních součástí z polotovarů, kdy je přebytečný materiál odebírán řezným nástrojem ve formě třísek. Dynamický vývoj technologií s sebou přinesl
VíceZÁKLADNÍ STUDIUM VLASTNOSTÍ A CHOVÁNÍ SYSTÉMŮ TENKÁ VRSTVA SKLO POMOCÍ INDENTAČNÍCH ZKOUŠEK
ZÁKLADNÍ STUDIUM VLASTNOSTÍ A CHOVÁNÍ SYSTÉMŮ TENKÁ VRSTVA SKLO POMOCÍ INDENTAČNÍCH ZKOUŠEK THE BASIC EVALUATION OF PROPERTIES AND BEHAVIOUR OF SYSTEMS THIN FILMS GLASS BY INDENTATION TESTS Ivo Štěpánek,
VíceCZ.1.07/1.1.30/01.0038 SPŠ
Monitorovací indikátor: 06.43.10 Počet nově vytvořených/inovovaných produktů Akce: Přednáška, KA 5 Číslo přednášky: 3 Téma: APLIKACE TENKÝCH VRSTEV NA OBRÁBĚCÍCH NÁSTROJÍCH Lektor: Ing. Jiří Hodač Třída/y:
VíceObrábění slitiny AlSi1Mg0,5Mn nástroji s progresivními tenkými vrstvami
Obrábění slitiny AlSi1Mg0,5Mn nástroji s progresivními tenkými vrstvami Antonín Kříž, Miroslav Zetek, Jan Matějka, Josef Formánek, Martina Sosnová, Jiří Hájek, Milan Vnouček Příspěvek vznikl na základě
VíceHODNOCENÍ MECHANICKÝCH VLASTNOSTÍ TENKOVRSTVÝCH SYSTÉMŮ Z GRAFU ZÁVISLOSTI MÍRY INFORMACE NA ZATÍŽENÍ
HODNOCENÍ MECHANICKÝCH VLASTNOSTÍ TENKOVRSTVÝCH SYSTÉMŮ Z GRAFU ZÁVISLOSTI MÍRY INFORMACE NA ZATÍŽENÍ ANALYSIS OF MECHANICAL PROPERTIES OF THIN FILMS SYSTEMS FROM DEPENDENCE OF KIND OF INFORMATION AND
VíceTEPLOTNÍ DEGRADACE TENKÝCH OTĚRUVZDORNÝCH PVD VRSTEV THERMAL DEGRADATION OF THIN WEAR RESISTANCE PVD COATINGS. Petr Beneš a Antonín Kříž b
TEPLOTNÍ DEGRADACE TENKÝCH OTĚRUVZDORNÝCH PVD VRSTEV THERMAL DEGRADATION OF THIN WEAR RESISTANCE PVD COATINGS Petr Beneš a Antonín Kříž b a ZÁPADOČESKÁ UNIVERZITA,FST,KMM Univerzitní 22, 306 14 Plzeň,
Více3.1 Druhy karbidů a povlaků od firmy Innotool
KARBIDY A POVLAKY 3.1 Druhy karbidů a povlaků od firmy Innotool 3.1.1 Nepovlakované karbidy IN04S IN05S IN10K IN15K IN30M K10-K20 M10-M20 K10-K25 K20-K50 Jemnozrnný karbid pro obrábění Al slitin s vyšším
VíceNauka o materiálu. Přednáška č.14 Kompozity
Nauka o materiálu Úvod Technické materiály, které jsou určeny k dalšímu technologickému zpracování zahrnují širokou škálu možného chemického složení, různou vnitřní stavbu a různé vlastnosti. Je nutno
VícePŘÍNOS METALOGRAFIE PŘI ŘEŠENÍ PROBLÉMŮ TEPELNÉHO ZPRACOVÁNÍ NÁSTROJOVÝCH OCELÍ. Antonín Kříž
PŘÍNOS METALOGRAFIE PŘI ŘEŠENÍ PROBLÉMŮ TEPELNÉHO ZPRACOVÁNÍ NÁSTROJOVÝCH OCELÍ Antonín Kříž Tento příspěvek vznikl na základě spolupráce s firmou Hofmeister s.r.o., řešením projektu FI-IM4/226. Místo,
VíceZMENY POVRCHOVÝCH MECHANICKÝCH VLASTNOSTÍ SYSTÉMU S TENKÝMI VRSTVAMI PO KOMBINOVANÉM NAMÁHÁNÍ. Roman Reindl, Ivo Štepánek
ZMENY POVRCHOVÝCH MECHANICKÝCH VLASTNOSTÍ SYSTÉMU S TENKÝMI VRSTVAMI PO KOMBINOVANÉM NAMÁHÁNÍ Roman Reindl, Ivo Štepánek Západoceská univerzita v Plzni, Univerzitní 22, 306 14 Plzen, CR, ivo.stepanek@volny.cz
VíceAnalýza PIN-on-DISC. Ing. Jiří Hájek Dr. Ing. Antonín Kříž ZÁPADOČESKÁ UNIVERZITA V PLZNI
Analýza PIN-on-DISC Ing. Jiří Hájek Dr. Ing. Antonín Kříž ZÁPADOČESKÁ UNIVERZITA V PLZNI 1/18 TRIBOLOGICKÝ PROCES Tribological process Factors that influence the process: loading, loading type, movement
VíceHodnocení korozí odolnosti systémů tenká vrstva substrát v prostředí kompresorů
Hodnocení korozí odolnosti systémů tenká vrstva substrát v prostředí kompresorů Analysis of Corrosion Resistance of Systems Thin Films Substrate in Compressors Environment Jiří Hána, Ivo Štěpánek, Radek
VíceNauka o materiálu. Přednáška č.12 Keramické materiály a anorganická nekovová skla
Nauka o materiálu Přednáška č.12 Keramické materiály a anorganická nekovová skla Úvod Keramika a nekovová skla jsou ve srovnání s kovy velmi křehké. Jejich pevnost v tahu je nízká a finálnímu lomu nepředchází
VíceTrvanlivost,obrobitelnost,opotřebení břitu
Střední průmyslová škola a Vyšší odborná škola technická Brno, Sokolská 1 Šablona: Název: Téma: Autor: Inovace a zkvalitnění výuky prostřednictvím ICT Obrábění Trvanlivost,obrobitelnost,opotřebení břitu
VíceInovační vrták pro strojírenský sektor
Vrtáky z tvrdokovu Inovační vrták pro strojírenský sektor PLUS8, NĚMECKÁ TECHNOLOGIE S ITALSKÝM SRDCEM. Výrobní zařízení a Centra pro výzkum a vývoj v Evropě a Severní Americe umožňují firmě Cruing nabízet
VíceTransfer inovácií 20/2011 2011
OBRÁBĚNÍ LASEREM KALENÉHO POVRCHU Ing. Miroslav Zetek, Ph.D. Ing. Ivana Česáková Ing. Josef Sklenička Katedra technologie obrábění Univerzitní 22, 306 14 Plzeň e-mail: mzetek@kto.zcu.cz Abstract The technology
VíceCYKLICKÁ VRYPOVÁ ZKOUŠKA PRO HODNOCENÍ VÝVOJE PORUŠENÍ A V APROXIMACI ZKOUŠKY OPOTŘEBENÍ. Markéta Podlahová, Ivo Štěpánek, Martin Hrdý
CYKLICKÁ VRYPOVÁ ZKOUŠKA PRO HODNOCENÍ VÝVOJE PORUŠENÍ A V APROXIMACI ZKOUŠKY OPOTŘEBENÍ. Markéta Podlahová, Ivo Štěpánek, Martin Hrdý Západočeská univerzita v Plzni, Univerzitní 22, 306 14 Plzeň, ČR,
VíceRozhodující vlastnosti nástrojových ocelí pro: POUŽITÍ. Charakteristika OPTIMÁLNÍ VÝKON NÁSTROJŮ VÝROBU NÁSTROJŮ VANCRON 40
1 VANCRON 40 2 Rozhodující vlastnosti nástrojových ocelí pro: OPTIMÁLNÍ VÝKON NÁSTROJŮ V mnoha aplikacích nástrojových ocelí pro práci za studena vyžadujeme povlakování povrchu, jako prevenci proti nalepování
VíceTEPLOTNÍ ODOLNOST TENKÝCH VRSTEV A JEJICH PŘÍNOS V OBRÁBĚNÍ TVRDÝCH OCELÍ. Antonín Kříž Petr Beneš Martina Sosonová Jiří Hájek
TEPLOTNÍ ODOLNOST TENKÝCH VRSTEV A JEJICH PŘÍNOS V OBRÁBĚNÍ TVRDÝCH OCELÍ Antonín Kříž Petr Beneš Martina Sosonová Jiří Hájek Na počátku byla co se kdy žs st a ne s obyčejná zvědavost, na de en po no ech
VíceCENÍK OSTŘENÍ A POVLAKOVÁNÍ
CENÍK OSTŘENÍ A POVLAKOVÁNÍ HSS Drážkovací fréza Prodloužená Prodloužená -12 108 Kč 166 Kč -12 247 Kč 370 Kč -20 154 Kč 232 Kč -20 305 Kč 459 Kč -30 215 Kč 321 Kč -30 443 Kč 668 Kč -40 292 Kč 439 Kč -40
VíceVÝROBKY PRÁŠKOVÉ METALURGIE
1 VÝROBKY PRÁŠKOVÉ METALURGIE Použití práškové metalurgie Prášková metalurgie umožňuje výrobu součástí z práškových směsí kovů navzájem neslévatelných (W-Cu, W-Ag), tj. v tekutém stavu nemísitelných nebo
VíceKONVENČNÍ FRÉZOVÁNÍ Zdeněk Zelinka
KONVENČNÍ FRÉZOVÁNÍ Zdeněk Zelinka Frézy VY_32_INOVACE_OVZ_1_05 OPVK 1.5 EU peníze středním školám CZ.1.07/1.500/34.0116 Modernizace výuky na učilišti Název školy Název šablony Předmět Tematický celek
VíceKontaktní cyklické testování materiálů pomocí IMPACT testeru. Antonín Kříž; Petr Beneš
Kontaktní cyklické testování materiálů pomocí IMPACT testeru Antonín Kříž; Petr Beneš V mnoha průmyslových aplikacích jsou součásti vystaveny intenzivním účinkům kontaktního namáhání Při kontaktním namáhání
VíceNÁSTROJE A TECHNOLOGIE ČESKÉ VÝROBKY VE ŠPIČKOVÉ KVALITĚ
2015/08 NÁSTROJE A TECHNOLOGIE ČESKÉ VÝROBKY VE ŠPIČKOVÉ KVALITĚ FRÉZY PRO VÝROBU FOREM MIKROFRÉZY 70 HRC KULOVÉ 70 HRC KULOVÉ 55 HRC KUŽELOVÉ 5 FRÉZY VÁLCOVÉ UNIVERZÁLNÍ HRUBOVACÍ DOKONČOVACÍ 70 HRC
VíceEVALUATION OF FAILURES AND MODIFICATION OF SYSTEMS THIN FILM BASIC MATERIAL TO THE DEPTH OF MATERIAL SYSTEMS
STUDIUM PORUŠENÍ A MODIFIKACE SYSTÉMŮ TENKÁ VRSTVA ZÁKLADNÍ MATERIÁL DO HLOUBKY MATERIÁLOVÝCH SYSTÉMŮ Abstrakt EVALUATION OF FAILURES AND MODIFICATION OF SYSTEMS THIN FILM BASIC MATERIAL TO THE DEPTH OF
VíceVLIV IONTOVÉHO BOMBARDU NA VLASTNOSTI SYSTÉMŮ VYTVÁŘENÝCH PVD TECHNOLOGIÍ. Antonín Kříž
Abstrakt VLIV IONTOVÉHO BOMBARDU NA VLASTNOSTI SYSTÉMŮ VYTVÁŘENÝCH PVD TECHNOLOGIÍ Antonín Kříž ZČU v Plzni, Univerzitní 22, 306 14 Plzeň, e-mail: kriz@kmm.zcu.cz Influence of ion bombardment upon properties
VíceKalení Pomocí laserového paprsku je možné rychle a kvalitně tepelně zušlechtit povrch materiálu až do hloubek v jednotkách milimetrů.
Kalení Pomocí laserového paprsku je možné rychle a kvalitně tepelně zušlechtit povrch materiálu až do hloubek v jednotkách milimetrů. Výhody laserového kalení: Nižší energetická náročnost (kalení pouze
VíceZáklady obrábění. Obrábění se uskutečňuje v soustavě stroj nástroj obrobek
Základy obrábění Obrábění je technologický proces, při kterém je přebytečná část materiálu oddělována z obrobku ve formě třísky břitem řezného nástroje. polotovar předmět, který se teprve bude obrábět
VíceMetalografie. Praktické příklady z materiálových expertíz. 4. cvičení
Metalografie Praktické příklady z materiálových expertíz 4. cvičení Obsah Protahovací trn Povrchově kalená součást Fréza Karbidické vyřádkování Cementovaná součást Pozinkovaná součást Pivní korunky Klíč
VíceODBORNÝ VÝCVIK VE 3. TISÍCILETÍ
Projekt: ODBORNÝ VÝCVIK VE 3. TISÍCILETÍ Téma: Nové typy nástrojů pro soustružení Obor: Obráběč kovů Ročník: 1. Zpracoval(a): Rožek Pavel Střední průmyslová škola Uherský Brod, 2010 Obsah Soustružení 3
VíceKATALOG NÁSTROJŮ PRO OBRÁBĚNÍ
2014/01 tool design & production KATALOG NÁSTROJŮ PRO OBRÁBĚNÍ FRÉZY PRO VÝROBU FOREM Z TVRDOKOVU FRÉZY VÁLCOVÉ NÁSTROJE PRO OBRÁBĚNÍ HLINÍKU NÁSTROJE PRO OBRÁBĚNÍ GRAFITU NÁSTROJE SPECIÁLNÍ A ZAKÁZKOVÉ
VíceIII/2 Inovace a zkvalitnění výuky prostřednictvím ICT. Sostružnické nože- učební materiál
Číslo projektu CZ.1.07/1.5.00/34.0514 Číslo a název šablony klíčové aktivity III/2 Inovace a zkvalitnění výuky prostřednictvím ICT Tematická oblast Soustružení, vy_32_inovace_ma_24_12 Autor Jaroslav Kopecký
VíceÚVOD DO INTEGRITY POVRCHU naše činnost. Antonín Kříž; Petr Beneš
ÚVOD DO INTEGRITY POVRCHU naše činnost Antonín Kříž; Petr Beneš 2.11.2012 Integrita 15.10.2012 Studentské práce sledující integritu povrchu Bakalářská práce David HUDA Vlastnosti a struktury progresivních
VíceHlavní skupina. Změna charakteristik. Označení Obráběný materiál Příklad užití a podmínky užití
Příloha č.4 Slinuté karbidy typu P P P01 P10 P20 P30 P40 P50 Ocel, ocelolitina Ocel, ocelolitina, temperovaná litina Ocel, ocelolitina s pískem a lunkry Ocel, ocelolitina, střední nebo nižší pevnosti,
VícePOŽÁRNÍ ODOLNOST DŘEVOBETONOVÉHO STROPU
Energeticky efektivní budovy 2015 sympozium Společnosti pro techniku prostředí 15. října 2015, Buštěhrad POŽÁRNÍ ODOLNOST DŘEVOBETONOVÉHO STROPU Eva Caldová 1), František Wald 1),2) 1) Univerzitní centrum
VíceCharakteristika. Vlastnosti. Použití FYZIKÁLNÍ VLASTNOSTI MECHANICKÉ VLASTNOSTI UNIMAX
1 UNIMAX 2 Charakteristika UNIMAX je Cr-Mo-V legovaná ocel pro práci v oblast zpracování plastů, pro kterou jsou charakteristické tyto vlastnosti: Vynikající houževnatost a tažnost ve všech průřezech Dobrá
VíceKarbidové technické frézy
autorizovaný distributor Karbidové technické frézy Rozšířený sortiment 2016 1 KARBIDOVÉ TECHNICKÉ FRÉZY Rozšířený sortiment 2016 PŘEDSTAVENÍ Doplňujeme řadu karbidových technických fréz vysoké kvality.
VíceC Cr N Mo Ni Mn 0,3% 15,0 % 0,5 % 0,95% 0,5% 1,0%
NÁSTROJOVÁ OCEL LC 200 N Certifikace dle ISO 9001 CHEMICKÉ SLOŽENÍ C Cr N Mo Ni Mn 0,3% 15,0 % 0,5 % 0,95% 0,5% 1,0% LC 200 N Je vysoce korozivzdorná, dusíkem legovaná nástrojová ocel s výtečnou houževnatostí
VíceHODNOCENÍ STÁRNUTÍ POVRCHU MATERIÁLU POMOCÍ INDENTACNÍCH MERENÍ
HODNOCENÍ STÁRNUTÍ POVRCHU MATERIÁLU POMOCÍ INDENTACNÍCH MERENÍ Marek Tengler, Ivo Štepánek Západoceská univerzita v Plzni, Univerzitní 22, 306 14 Plzen, CR, ivo.stepanek@volny.cz Abstrakt Príspevek se
VíceVLIV SVAROVÉHO SPOJE NA VLASTNOSTI NANÁŠENÝCH TENKÝCH VRSTEV TIN INFLUENCE OF WELDING ON PROPERTIES DEPOSITED THIN FILMS TIN
VLIV SVAROVÉHO SPOJE NA VLASTNOSTI NANÁŠENÝCH TENKÝCH VRSTEV TIN INFLUENCE OF WELDING ON PROPERTIES DEPOSITED THIN FILMS TIN Lenka Pourová a Radek Němec b Ivo Štěpánek c a) Západočeská univerzita v Plzni,
VíceASX445 NÁSTROJE NOVINKY. Stabilní čelní frézování při vysokém zatížení B017CZ. Čelní fréza. 2014.01 Aktualizace
NÁSTROJE NOVINKY 2014.01 Aktualizace B017CZ Čelní fréza Stabilní čelní frézování při vysokém zatížení Mechanismus destičky AFI (Anti Fly Insert) ze slinutého karbidu. Výkonný řez pro lepší účinnost. Těleso
VíceRYCHLOŘEZNÉ NÁSTROJOVÉ OCELI
RYCHLOŘEZNÉ NÁSTROJOVÉ OCELI Významnou složkou nabídky nástrojových ocelí společnosti Bohdan Bolzano s.r.o. jsou nástrojové oceli rychlořezné, vyráběné jak konvenčně, tak i metodou práškové metalurgie.
VíceLETECKÉ MATERIÁLY. Úvod do předmětu
LETECKÉ MATERIÁLY Úvod do předmětu Historický vývoj leteckých konstrukčních materiálů Uplatnění konstrukčních materiálů souvisí s pevnostními koncepcemi leteckých konstrukcí Pevnostní koncepce leteckých
VíceZKOUŠKY MIKROLEGOVANÝCH OCELÍ DOMEX 700MC
Sborník str. 392-400 ZKOUŠKY MIKROLEGOVANÝCH OCELÍ DOMEX 700MC Antonín Kříž Výzkumné centrum kolejových vozidel, ZČU v Plzni,Univerzitní 22, 306 14, Česká republika, kriz@kmm.zcu.cz Požadavky kladené dnešními
VíceVLIV VYBRANÝCH PARAMETRŮ TECHNOLOGICKÉHO PROCESU NA VLASTNOSTI A CHOVÁNÍ SYSTÉMŮ TENKÁ VRSTVA SUBSTRÁT
VLIV VYBRANÝCH PARAMETRŮ TECHNOLOGICKÉHO PROCESU NA VLASTNOSTI A CHOVÁNÍ SYSTÉMŮ TENKÁ VRSTVA SUBSTRÁT THE INFLUENCES OF SELECTED PARAMETERS OF TECHNOLOGICAL PROCESS ON PROPERTIES AND BEHAVIOUR OF SYSTEMS
Více1 Moderní nástrojové materiály
1 Řezné materiály jsou podle ISO 513 členěné do šesti základních skupin, podle typu namáhání břitu. - Skupina P zahrnuje nástrojové materiály určené k obrábění většiny ocelí, které dávají dlouhou třísku
Víceodolnost M9315 M9325 M9340 nové frézovací materiály www.pramet.com
odolnost www.pramet.com nové frézovací materiály řady M93 s MT-CVD povlakem P M Materiál je členem nové UP!GRADE GENERACE materiálů. Jedná se o frézovací materiál vyvinutý pro dosažení vysoké produktivity
VíceINTEGRITA POVRCHU A JEJÍ VÝZNAM PRO POSOUZENÍ VHODNOSTI DANÉ PLOCHY PRO JEJÍ FUNKCI Prof. Ing. Bohumil Bumbálek, CSc
INTEGRITA POVRCHU A JEJÍ VÝZNAM PRO POSOUZENÍ VHODNOSTI DANÉ PLOCHY PRO JEJÍ FUNKCI Prof. Ing. Bohumil Bumbálek, CSc Současné trendy v rozvoji výrobních systémů se dají charakterizovat snahou o zvyšování
VíceZÁPADOČESKÁ UNIVERZITA V PLZNI FAKULTA STROJNÍ
ZÁPADOČESKÁ UNIVERZITA V PLZNI FAKULTA STROJNÍ Studijní program: B2301 Strojní inženýrství Studijní zaměření: Strojírenská technologie-technologie obrábění BAKALÁŘSKÁ PRÁCE Přesné obrábění vnějších válcových
VícePosouzení stavu rychlořezné oceli protahovacího trnu
Posouzení stavu rychlořezné oceli protahovacího trnu ČSN 19 830 zušlechtěno dle předpisů pro danou ocel tj. kaleno a 3x popuštěno a) b) Obr.č. 1 a) Poškozený zub protahovacího trnu; b) Zdravý zub druhá
VíceCOMPARISON PROPERTIES AND BEHAVIOUR OF SYSTEM WITH THIN FILMS PREPARED BY DIFFERENT TECHNOLOGIES
POROVNÁNÍ VLASTNOSTÍ A CHOVÁNÍ SYSTÉMŮ S TENKÝMI VRSTVAMI Z RŮZNÝCH TECHNOLOGICKÝCH PROCESŮ COMPARISON PROPERTIES AND BEHAVIOUR OF SYSTEM WITH THIN FILMS PREPARED BY DIFFERENT TECHNOLOGIES Ivo Štěpánek
VíceKonstrukce soustružnického nože s VBD pomocí SW Catia V5 SVOČ FST 2009. Marek Urban (marekurban@seznam.cz)
Konstrukce soustružnického nože s VBD pomocí SW Catia V5 SVOČ FST 2009 Marek Urban (marekurban@seznam.cz) 1 Úvod Z mnoha pohledů je soustružení nejjednodušší formou obrábění, kde pomocí jednobřitého nástroje
VíceInfo Přehled šroubovitých vrtáků VHM (I) Vrtací nářadí. Doporučení použití W = vhodné X = omezeně vhodné Hliník > 10% Si W W W W W W W W
Inklusive Info Přehled šroubovitých vrtáků (I) Značka 0 0 0 0 0 0 0 0 Závodní norma Závodní norma Závodní norma Závodní norma 6539 6539 6539 6539 5 x D Skládaný vrták Skládaný vrták Číslo položky 11016
VíceEVALUATION OF SPECIFIC FAILURES OF SYSTEMS THIN FILM SUBSTRATE FROM SCRATCH INDENTATION IN DETAIL
DETAILNÍ STUDIUM SPECIFICKÝCH PORUŠENÍ SYSTÉMŮ TENKÁ VRSTVA SUBSTRÁT PŘI VRYPOVÉ INDENTACI EVALUATION OF SPECIFIC FAILURES OF SYSTEMS THIN FILM SUBSTRATE FROM SCRATCH INDENTATION IN DETAIL Kateřina Macháčková,
VíceCPM REX 45 (HS) NÁSTROJOVÁ OCEL. Certifikace dle ISO 9001 CHEMICKÉ SLOŽENÍ CPM REX 45. Typické oblasti použití FYZIKÁLNÍ VLASTNOSTI.
NÁSTROJOVÁ OCEL CPM REX 45 (HS) Certifikace dle ISO 9001 CHEMICKÉ SLOŽENÍ C Cr V Mo W Co S 1,30% 4,05 % 3,05 % 5,00% 6,25% 8,00% 0,06 % (provedení HS: 0,22 %) CPM REX 45 je vysokovýkonná, kobaltová rychlořezná
VíceHODNOCENÍ KOMBINOVANÉHO NAMÁHÁNÍ SYSTÉMŮ TENKÁ VRSTVA SUBSTRÁT NA VYSOKOTEPLOTNÍM TRIBOMETRU
HODNOCENÍ KOMBINOVANÉHO NAMÁHÁNÍ SYSTÉMŮ TENKÁ VRSTVA SUBSTRÁT NA VYSOKOTEPLOTNÍM TRIBOMETRU ANALYSIS OF COMBINATION STRESS OF SYSTEMS THIN FILM SUBSTRATE BY HIGH TEMPERATURE TRIBOMETER Roman Reindl a
VíceNÁVRH MATERIÁLU A POVRCHOVÉ ÚPRAVY PRO ŘEZNÉ NÁSTROJE URČENÝCH K OBRÁBĚNÍ PRYŽOVÝCH HADIC ZPEVNĚNÝCH KEVLAREM
NÁVRH MATERIÁLU A POVRCHOVÉ ÚPRAVY PRO ŘEZNÉ NÁSTROJE URČENÝCH K OBRÁBĚNÍ PRYŽOVÝCH HADIC ZPEVNĚNÝCH KEVLAREM Bc. Jiří Hodač Západočeská univerzita v Plzni, Univerzitní 8, 306 14 Plzeň Česká republika
VíceC Cr N Mo Ni Mn 0,3% 14,0 % 0,4 % 0,1% 0,4% 0,5%
NÁSTROJOVÁ OCEL LC 185 MP Certifikace dle ISO 9001 CHEMICKÉ SLOŽENÍ C Cr N Mo Ni Mn 0,3% 14,0 % 0,4 % 0,1% 0,4% 0,5% LC 185 MP Je dusíkem legovaná, korozivzdorná ocel typu matrix s excelentní leštitelností.
VíceŘezné materiály www. www t. u t n u g n a g loy o. y c. z c
Řezné materiály www.tungaloy.cz PRODUKTY Povlakované karbidy CVD A002 Povlakované karbidy PVD A003 Keramika A005 Cermety A005 CBN (T-CBN) A006 PCD (T-DIA) A007 Nepovlakované slinuté karbidy A007 Tungaloy
VíceVrtání v oblasti High-End vylepšená technologie povlakování Dragonskin značně zvýší pracovní výkon vrtáků WTX Speed a WTX Feed
New Září 2018 Nové produkty pro obráběcí techniky WTX Speed WTX Feed Vrtání v oblasti High-End vylepšená technologie povlakování Dragonskin značně zvýší pracovní výkon vrtáků WTX Speed a WTX Feed www.wnt.com
VíceANALÝZA POVLAKOVANÝCH POVRCHŮ ŘEZNÝCH NÁSTROJŮ
Středoškolská technika 2019 Setkání a prezentace prací středoškolských studentů na ČVUT ANALÝZA POVLAKOVANÝCH POVRCHŮ ŘEZNÝCH NÁSTROJŮ Jakub Chlaň, Matouš Hyk, Lukáš Procházka Střední škola elektrotechniky
VíceVÝZKUM MOŽNOSTÍ ZVÝŠENÍ ŽIVOTNOSTI LOŽISEK CESTOU POVRCHOVÝCH ÚPRAV
VÝZKUM MOŽNOSTÍ ZVÝŠENÍ ŽIVOTNOSTI LOŽISEK CESTOU POVRCHOVÝCH ÚPRAV RESEARCH INTO POSSIBILITY OF INCREASING SERVICE LIFE OF BEARINGS VIA SURFACE TREATMENT Zdeněk Spotz a Jiří Švejcar a Vratislav Hlaváček
VíceTESTOVÁNÍ VLIVU INDIKAČNÍCH KAPALIN NA KŘEHKOLOMOVÉ VLASTNOSTI SKLOVITÝCH SMALTOVÝCH POVLAKŮ
TESTOVÁNÍ VLIVU INDIKAČNÍCH KAPALIN NA KŘEHKOLOMOVÉ VLASTNOSTI SKLOVITÝCH SMALTOVÝCH POVLAKŮ TESTING OF THE INFLUENCE OF THE INDICATING LIQUIDS ON BREAKED PROPERTIES OF VITREOUS ENAMEL COATINGS Kamila
VíceMateriály. Produkty 1-2 1-4 1-6 1-8 1-10 1-12 1-13 1-14 1-15
Produkty Přehled řezných materiálů... Povlakovaný karbid / CVD... Povlakovaný karbid/ PVD... Cermet... PCBN (T-CBN)... PCD (T-DIA)... Keramika... Nepovlakovaný slinutý karbid... Submikronové slinuté karbidy...
VíceEXPERIMENTÁLNÍ METODY V OBRÁBĚNÍ
ZÁPADOČESKÁ UNIVERZITA FAKULTA STROJNÍ KATEDRA TECHNOLOGIE OBRÁBĚNÍ EXPERIMENTÁLNÍ METODY V OBRÁBĚNÍ ÚLOHA č. 4 (Skupina č. 1) OPTIMALIZACE ŘEZNÉHO PROCESU (Trvanlivost břitu, dlouhodobá zkouška obrobitelnosti
VíceSTUDIUM MECHANICKÉHO CHOVÁNÍ ROZDÍLNÝCH SYSTÉMŮ TENKÁ VRSTVA SKLO POMOCÍ INDENTAČNÍCH ZKOUŠEK
STUDIUM MECHANICKÉHO CHOVÁNÍ ROZDÍLNÝCH SYSTÉMŮ TENKÁ VRSTVA SKLO POMOCÍ INDENTAČNÍCH ZKOUŠEK EVALUATION OF MECHANICAL BEHAVIOUR OF DIFFERENT SYSTEMS THIN FILM GLASS BY INDENTATION TESTS Ivo Štěpánek,
VíceEVALUATION OF INFLUENCE PREPARING OF SURFACE OF SUBSTRATE ON BEHAVIOUR OF SYSTEMS THIN FILM SUBSTRATE
STUDIUM VLIVU PŘÍPRAVY POVRCHU SUBSTRÁTU NA CHOVÁNÍ SYSTÉMŮ TENKÁ VRSTVA SUBSTRÁT EVALUATION OF INFLUENCE PREPARING OF SURFACE OF SUBSTRATE ON BEHAVIOUR OF SYSTEMS THIN FILM SUBSTRATE Zdeněk Beneš, Ivo
VíceVliv volby nástroje na parametry řezného procesu. Lukáš Matula
Vliv volby nástroje na parametry řezného procesu Lukáš Matula Bakalářská práce 2012 ABSTRAKT Tato práce se zaměřuje na proces frézování a testování různých frézovacích nástrojů. Zkoumá různé typy nástrojů
VíceCharakteristika. Použití TVÁŘECÍ NÁSTROJE STŘÍHÁNÍ RIGOR
1 RIGOR 2 Charakteristika RIGOR je na vzduchu nebo v oleji kalitelná Cr-Mo-V legovaná ocel, pro kterou jsou charakteristické tyto vlastnosti: Dobrá obrobitelnost Vysoká rozměrová stálost po kalení Vysoká
VíceEMCO Sinumerik 810 M - frézování
Střední průmyslová škola a Vyšší odborná škola technická Brno, Sokolská 1 Šablona: Inovace a zkvalitnění výuky prostřednictvím ICT Název: Téma: Autor: Číslo: Anotace: EMCO Sinumerik 810 M - frézování Určení
VícePOROVNÁNÍ VLIVU DEPOSICE TENKÝCH VRSTEV A NAVAŘOVÁNÍ NA DEGRADACI ZÁKLADNÍHO MATERIÁLU
POROVNÁNÍ VLIVU DEPOSICE TENKÝCH VRSTEV A NAVAŘOVÁNÍ NA DEGRADACI ZÁKLADNÍHO MATERIÁLU COMPARISON OF INFLUENCES OF DEPOSITION THIN FILMS AND WELDING ON DEGRADATION OF BASIC MATERIAL Monika Hadáčková a
VíceŘezná keramika. Moderní a produktivní způsob obrábění žárovzdorných slitin
Řezná keramika Moderní a produktivní způsob obrábění žárovzdorných slitin Obrábění pomocí řezné keramiky Použití Keramické třídy je možné použít pro široký okruh aplikací a materiálů, přičemž nejčastěji
VíceObrobený povrch a jeho vliv na užitné vlastnosti Antonín Kříž
Obrobený povrch a jeho vliv na užitné vlastnosti Antonín Kříž Seminář Inovace řezných nástrojů a technologií obrábění Cech brusičů a výrobců nástrojů HOFMEISTER s.r.o. - výrobce speciálního nářadí ZČU
VíceCOMPARISON OF SYSTEM THIN FILM SUBSTRATE WITH VERY DIFFERENT RESISTANCE DURING INDENTATION TESTS. Matyáš Novák, Ivo Štěpánek
POROVNÁNÍ SYSTÉMŮ TENKÁ VRSTVA SUBSTRÁT S VELICE ROZDÍLNOU ODOLNOSTÍ PŘI INDENTAČNÍCH ZKOUŠKÁCH COMPARISON OF SYSTEM THIN FILM SUBSTRATE WITH VERY DIFFERENT RESISTANCE DURING INDENTATION TESTS Matyáš Novák,
VíceVliv povrchu na užitné vlastnosti výrobku
Vliv povrchu na užitné vlastnosti výrobku Antonín Kříž Tento příspěvek vznikl na základě dlouhodobé spolupráce s průmyslovou společností HOFMEISTER s.r.o. a řešení průmyslového projektu FI-IM4/226, který
VíceNÁSTROJOVÉ OCELI CPM 10 V
NÁSTROJOVÁ OCEL CPM 10 V CERTIFIKACE DLE ISO 9001 Chem. složení C 2,45 % Cr 5,25 % V 9,75 % Mo 1,30 % Mn 0,50 % Si 0,90 % CPM 10 V Je jedinečná vysokovýkonná ocel, vyráběná společností Crucible (USA) metodou
VíceTENKÉ VRSTVY NA ŘEZNÝCH NÁSTROJÍCH PRO TĚŽKOOBROBITELNÉ PLASTY VÝVOJ TENKÝCH VRSTEV APLIKOVANÝCH NA ŘEZNÝCH NÁSTROJÍCH
TENKÉ VRSTVY NA ŘEZNÝCH NÁSTROJÍCH PRO TĚŽKOOBROBITELNÉ PLASTY VÝVOJ TENKÝCH VRSTEV APLIKOVANÝCH NA ŘEZNÝCH NÁSTROJÍCH Tato přednáška vznikla sloučením dvou původních příspěvků, které jsou uvedeny ve sborníku
VíceVLASTNOSTI KOMPOZITNÍCH POVLAKŮ S KATODICKY VYLUČOVANOU MATRICÍ
VLASTNOSTI KOMPOZITNÍCH POVLAKŮ S KATODICKY VYLUČOVANOU MATRICÍ Pavel Adamiš Miroslav Mohyla Vysoká škola báňská -Technická univerzita Ostrava, 17. listopadu 15, 708 33, Ostrava - Poruba, ČR Abstract In
Více